Crystals of bismuth antimonides are synthesized by melting bismuth and antimony together under inert gas or vacuum. Zone melting is used to decrease the concentration of impurities.^[4] When synthesizing single crystals of bismuth antimonides, it is important that impurities are removed from the samples, as oxidation occurring at the impurities leads to polycrystalline growth.^[1]

Topological insulator edit

Pure bismuth is a semimetal, containing a small band gap, which leads to it having a relatively high conductivity (7.7×10⁵ S/m at 20 °C). When the bismuth is doped with antimony, the conduction band decreases in energy and the valence band increases in energy. At an antimony concentration of 4%, the two bands intersect, forming a Dirac point^[2] (which is defined as a point where the conduction and valence bands intersect). Further increases in the concentration of antimony result in a band inversion, in which the energy of the valence band becomes greater than that of the conduction band at specific momenta. Between Sb concentrations of 7 and 22%, the bands no longer intersect, and the Bi_1−xSb_x becomes an inverted-band insulator.^[6] It is at these higher concentrations of Sb that the band gap in the surface states vanishes, and the material thus conducts at its surface.^[2]

Superconductor edit

The highest temperatures at which Bi_0.4Sb_0.6, as a thin film of thicknesses 150–1350 Å, superconducts (the critical temperature T_c) is approximately 2 K.^[3] Single crystal Bi_0.935Sb_0.065 can superconduct at slightly higher temperatures, and at 4.2 K, its critical magnetic field B_c (the maximum magnetic field that the superconductor can expel) of 1.6 T at 4.2 K.^[7]

Semiconductor edit

Electron mobility is one important parameter describing semiconductors because it describes the rate at which electrons can travel through the semiconductor. At 40 K, electron mobility ranged from 4.9×10⁵ cm²/V·s at an antimony concentration of 0 to 2.4×10⁵ cm²/V·s at an antimony concentration of 7.2%.^[1] This is much greater than the electron mobility of other common semiconductors like silicon, which is 1400 cm²/V·s at room temperature.^[8]

Another important parameter of Bi_1−xSb_x is the effective electron mass (EEM), a measure of the ratio of the acceleration of an electron to the force applied to an electron. The effective electron mass is 2×10⁻³ m_e for x = 0.11 and 9×10⁻⁴ m_e at x = 0.06.^[2] This is much less than the electron effective mass in many common semiconductors (1.09 in Si at 300 K, 0.55 in Ge, and 0.067 in GaAs). A low EEM is good for Thermophotovoltaic applications.

Thermoelectric edit

Bismuth antimonides are used as the n-type legs in many thermoelectric devices below room temperature. The thermoelectric efficiency, given by its figure of merit z_T = σS²T/λ, where S is the Seebeck coefficient, λ is the thermal conductivity, and σ is the electrical conductivity, describes the ratio of the energy provided by the thermoelectric to the heat absorbed by the device. At 80 K, the figure of merit (z_T) for Bi_1−xSb_x peaks at 6.5×10⁻³ K⁻¹ when x = 0.15.^[4] Also, the Seebeck coefficient (the ratio of the potential difference between ends of a material to the temperature difference between the sides) at 80 K of Bi_0.9Sb_0.1 is −140 μV/K, much lower than the Seebeck coefficient of pure bismuth, −50 μV/K.^[9]