The T-DCF amplifier was first conceived and demonstrated at Tampere University in the research group of Professor Oleg Okhotnikov in 2008. The technology was granted a patent in 2013 as a means to overcome the nonlinear optical effects which previously limited the power-scaling of fiber lasers and fiber amplifiers.^[1]

Reduced non-linear effect distortion in fiber amplification edit

Increasing the diameter of a cylindrical optical fiber amplifiers generally increases the level of non-linear effects such as stimulated Brillouin scattering.^[2] The result of forming a tapered geometry double-clad fiber is that the light introduced into the thin end propagates in a wide core without changing the mode content.^[3] Consequently, the use of T-DCF for optical amplification in a multi-mode fiber maintains good beam quality by elevating the thresholds of stimulation of non-linear effects including Brillouin and Raman scattering and spontaneous emission. Using tapered fiber with thick end core diameters of up to 200 µm with a 0.11 numerical aperture and record peak power and energy amplification levels 60 ps pulses with 300 µJ energy free of non-linear distortions have been reported.^[4]

High absorption of pump light edit

The double-clad structure of the fiber means the core can be pumped with higher-power than could be propagated in the fiber. The absorption and conversion of pump light per unit length is increased in the tapered fiber compared to cylindrical fibers with similar levels of active ion doping. This is due to the improved clad mode mixing and the higher absorption at the thicker end of the taper due to the much thicker cladding which also means the rare earth ion dopants are beneficially concentrated at the wide end of a T-DCF, since the geometry defines their presence as directly proportional to the square of the diameter.^[5] This higher absorption enables amplification of ultrafast lasers by very short amplifiers only tens of centimeters long, providing high fidelity ultrashort pulse amplification.

Simplicity of production edit

One of the significant advantages of T-DCF is the simplicity of production. The preform production for special high power fibers (microstructured rod type fibers, 3C or LCF fibers) involves complex technology and strict structural requirements. Conversely, T-DCF is made using standard fiber preforms. Simple production techniques of varying of the drawing speed during the pulling process leads to the fiber diameter changing along its length. T-DCF production is only marginally more complex than the production of a regular active fiber.