Aerogel: Gel comprising a microporous solid in which the dispersed phase is a gas.
Note 1: Microporous silica, microporous glass, and zeolites are common examples of aerogels.
Note 2: Corrected from ref., where the definition is a repetition of the incorrect definition of a gel followed by an inexplicit reference to the porosity of the structure.
A flower is on a piece of aerogel which is suspended over a flame from a Bunsen burner. Aerogel has excellent insulating properties, and the flower is protected from the flame.
Despite the name, aerogels are solid, rigid, and dry materials that do not resemble a gel in their physical properties: the name comes from the fact that they are made from gels. Pressing softly on an aerogel typically does not leave even a minor mark; pressing more firmly will leave a permanent depression. Pressing extremely firmly will cause a catastrophic breakdown in the sparse structure, causing it to shatter like glass (a property known as friability), although more modern variations do not suffer from this. Despite the fact that it is prone to shattering, it is very strong structurally. Its impressive load-bearing abilities are due to the dendritic microstructure, in which spherical particles of average size 2–5 nm are fused together into clusters. These clusters form a three-dimensional highly porous structure of almost fractal chains, with pores just under 100 nm. The average size and density of the pores can be controlled during the manufacturing process.
Aerogel is a material that is 99.8% air. Aerogels have a porous solid network that contains air pockets, with the air pockets taking up the majority of space within the material. The dearth of solid material allows aerogel to be almost weightless.
Aerogels are good thermal insulators because they almost nullify two of the three methods of heat transfer – conduction (they are mostly composed of insulating gas) and convection (the microstructure prevents net gas movement). They are good conductive insulators because they are composed almost entirely of gases, which are very poor heat conductors. (Silica aerogel is an especially good insulator because silica is also a poor conductor of heat; a metallic or carbon aerogel, on the other hand, would be less effective.) They are good convective inhibitors because air cannot circulate through the lattice. Aerogels are poor radiative insulators because infrared radiation (which transfers heat) passes through them.
Owing to its hygroscopic nature, aerogel feels dry and acts as a strong desiccant. People handling aerogel for extended periods should wear gloves to prevent the appearance of dry brittle spots on their skin.
The slight color it does have is due to Rayleigh scattering of the shorter wavelengths of visible light by the nano-sized dendritic structure. This causes it to appear smoky blue against dark backgrounds and yellowish against bright backgrounds.
Aerogels by themselves are hydrophilic, and if they absorb moisture they usually suffer a structural change, such as contraction, and deteriorate, but degradation can be prevented by making them hydrophobic, via a chemical treatment. Aerogels with hydrophobic interiors are less susceptible to degradation than aerogels with only an outer hydrophobic layer, especially if a crack penetrates the surface.
Aerogels may have a thermal conductivity smaller than that of the gas they contain. This is caused by the Knudsen effect, a reduction of thermal conductivity in gases when the size of the cavity encompassing the gas becomes comparable to the mean free path. Effectively, the cavity restricts the movement of the gas particles, decreasing the thermal conductivity in addition to eliminating convection. For example, thermal conductivity of air is about 25 mW·m−1·K−1 at STP and in a large container, but decreases to about 5 mW·m−1·K−1 in a pore 30 nanometers in diameter.
Aerogel structure results from a sol-gelpolymerization, which is when monomers (simple molecules) react with other monomers to form a sol or a substance that consists of bonded, cross-linked macromolecules with deposits of liquid solution among them. When the material is critically heated, the liquid evaporates and the bonded, cross-linked macromolecule frame is left behind. The result of the polymerization and critical heating is the creation of a material that has a porous strong structure classified as aerogel. Variations in synthesis can alter the surface area and pore size of the aerogel. The smaller the pore size the more susceptible the aerogel is to fracture.
Aerogel contains particles that are 2–5 nm in diameter. After the process of creating aerogel, it will contain a large amount of hydroxyl groups on the surface. The hydroxyl groups can cause a strong reaction when the aerogel is placed in water, causing it to catastrophically dissolve in the water. One way to waterproof the hydrophilic aerogel is by soaking the aerogel with some chemical base that will replace the surface hydroxyl groups (–OH) with non-polar groups (–OR), a process which is most effective when R is an aliphatic group.
Porosity of aerogel
There are several ways to determine the porosity of aerogel: the three main methods are gas adsorption, mercury porosimetry, and scattering method. In gas absorption, nitrogen at its boiling point is adsorbed into the aerogel sample. The gas being adsorbed is dependent on the size of the pores within the sample and on the partial pressure of the gas relative to its saturation pressure. The volume of the gas adsorbed is measured by using the Brunauer, Emmit and Teller formula (BET), which gives the specific surface area of the sample. At high partial pressure in the adsorption/desorption the Kelvin equation gives the pore size distribution of the sample. In mercury porosimetry, the mercury is forced into the aerogel porous system to determine the pores' size, but this method is highly inefficient since the solid frame of aerogel will collapse from the high compressive force. The scattering method involves the angle-dependent deflection of radiation within the aerogel sample. The sample can be solid particles or pores. The radiation goes into the material and determines the fractal geometry of the aerogel pore network. The best radiation wavelengths to use are X-rays and neutrons. Aerogel is also an open porous network: the difference between an open porous network and a closed porous network is that in the open network, gases can enter and leave the substance without any limitation, while a closed porous network traps the gases within the material forcing them to stay within the pores. The high porosity and surface area of silica aerogels allow them to be used in a variety of environmental filtration applications.
A 2.5 kg brick is supported by a piece of aerogel with a mass of 2 g.
Silica aerogel is the most common type of aerogel, and the primary type in use or study. It is silica-based and can be derived from silica gel or by a modified Stober process. The lowest-density silica nanofoam weighs 1,000 g/m3, which is the evacuated version of the record-aerogel of 1,900 g/m3. The density of air is 1,200 g/m3 (at 20 °C and 1 atm). As of 2013[update], aerographene had a lower density at 160 g/m3, or 13% the density of air at room temperature.
The silica solidifies into three-dimensional, intertwined clusters that make up only 3% of the volume. Conduction through the solid is therefore very low. The remaining 97% of the volume is composed of air in extremely small nanopores. The air has little room to move, inhibiting both convection and gas-phase conduction.
Silica aerogel also has a high optical transmission of ~99% and a low refractive index of ~1.05. It is very robust with respect to high power input beam in continuous wave regime and does not show any boiling or melting phenomena.  This property permits to study high intensity nonlinear waves in the presence of disorder in regimes typically unaccessible by liquid materials, making it promising material for nonlinear optics.
This aerogel has remarkable thermal insulative properties, having an extremely low thermal conductivity: from 0.03 W·m−1·K−1 in atmospheric pressure down to 0.004 W·m−1·K−1 in modest vacuum, which correspond to R-values of 14 to 105 (US customary) or 3.0 to 22.2 (metric) for 3.5 in (89 mm) thickness. For comparison, typical wall insulation is 13 (US customary) or 2.7 (metric) for the same thickness. Its melting point is 1,473 K (1,200 °C; 2,192 °F). It is also worth noting that even lower conductivities have been reported for experimentally produced monolithic samples in the literature, reaching 0.009 W·m−1·K−1 at 1atm.
Carbon aerogels are composed of particles with sizes in the nanometer range, covalently bonded together. They have very high porosity (over 50%, with pore diameter under 100 nm) and surface areas ranging between 400 and 1,000 m2/g. They are often manufactured as composite paper: non-woven paper made of carbon fibers, impregnated with resorcinol–formaldehyde aerogel, and pyrolyzed. Depending on the density, carbon aerogels may be electrically conductive, making composite aerogel paper useful for electrodes in capacitors or deionization electrodes. Due to their extremely high surface area, carbon aerogels are used to create supercapacitors, with values ranging up to thousands of farads based on a capacitance density of 104 F/g and 77 F/cm3. Carbon aerogels are also extremely "black" in the infrared spectrum, reflecting only 0.3% of radiation between 250 nm and 14.3 µm, making them efficient for solar energy collectors.
The term "aerogel" to describe airy masses of carbon nanotubes produced through certain chemical vapor deposition techniques is incorrect. Such materials can be spun into fibers with strength greater than Kevlar, and unique electrical properties. These materials are not aerogels, however, since they do not have a monolithic internal structure and do not have the regular pore structure characteristic of aerogels.
Metal oxide aerogels are used as catalysts in various chemical reactions/transformations or as precursors for other materials.
Aerogels made with aluminium oxide are known as alumina aerogels. These aerogels are used as catalysts, especially when "doped" with a metal other than aluminium. Nickel–alumina aerogel is the most common combination. Alumina aerogels are also being considered by NASA for capturing hypervelocity particles; a formulation doped with gadolinium and terbium could fluoresce at the particle impact site, with the amount of fluorescence dependent on impact energy.
One of the most notable differences between silica aerogels and metal oxide aerogel is that metal oxide aerogels are often variedly colored.
Chalcogel is an aerogel made of chalcogens (the column of elements on the periodic table beginning with oxygen) such as sulfur, selenium and other elements. Metals less expensive than platinum have been used in its creation.
Aerogel performance may be augmented for a specific application by the addition of dopants, reinforcing structures and hybridizing compounds. Aspen Aerogels makes products such as Spaceloft which are composites of aerogel with some kind of fibrous batting.
The "Stardust" dust collector with aerogel blocks. (NASA)
Cosmic dust caught in aerogel blocks from "Stardust". (NASA)
Cosmic dust tracks from a comet caught in aerogel blocks from "Stardust". (NASA)
Oil absorption by an aerogel. (Scientific Reports)
An aerogel held up by hair. (Scientific Reports)
An aerogel holding crayons, with a flame lit underneath, demonstrating its excellent insulation from heat. (NASA)
A material used in impedance matchers for transducers, speakers and range finders.
According to Hindawi's Journal of Nanomaterials, aerogels are used for more flexible materials such as clothing and blankets: "Commercial manufacture of aerogel 'blankets' began around the year 2000, combining silica aerogel and fibrous reinforcement that turns the brittle aerogel into a durable, flexible material. The mechanical and thermal properties of the product may be varied based upon the choice of reinforcing fibers, the aerogel matrix and opacification additives included in the composite."
Silica aerogel has been used to capture cosmic dust, also known as space dust.NASA used an aerogel to trap space dust particles aboard the Stardust spacecraft. These aerogel dust collectors have very low mass. The particles vaporize on impact with solids and pass through gases, but can be trapped in aerogels. NASA also used aerogel for thermal insulation for the Mars rovers.
The US Navy evaluated use of aerogels in undergarments as passive thermal protection for divers. Similarly, aerogels have been used by NASA for insulating space suits.
Metal–aerogel nanocomposites prepared by impregnating the hydrogel with solution containing ions of a transition metal and irradiating the result with gamma rays, precipitates nanoparticles of the metal. Such composites can be used as catalysts, sensors, electromagnetic shielding, and in waste disposal. A prospective use of platinum-on-carbon catalysts is in fuel cells.
As a drug delivery system owing to its biocompatibility. Due to its high surface area and porous structure, drugs can be adsorbed from supercritical CO 2. The release rate of the drugs can be tailored by varying the properties of the aerogel.
Carbon aerogels are used in the construction of small electrochemical double layer supercapacitors. Due to the high surface area of the aerogel, these capacitors can be 1/2000th to 1/5000th the size of similarly rated electrolytic capacitors. According to Hindawi's Journal of Nanomaterials, "Aerogel supercapacitors can have a very low impedance compared to normal supercapacitors and can absorb or produce very high peak currents. At present, such capacitors are polarity-sensitive and need to be wired in series if a working voltage of greater than about 2.75 V is needed."
In water purification, chalcogels have shown promise in absorbing the heavy metal pollutants mercury, lead, and cadmium from water. Aerogels may be used to separate oil from water, which could for example be used to respond to oil spills. Aerogels may be used to disinfect water, killing bacteria.
In aircraft de-icing, a new proposal uses a carbon nanotube aerogel. A thin filament is spun on a winder to create a 10 micron-thick film. The amount of material needed to cover the wings of a jumbo jet weighs 80 grams (2.8 oz). Aerogel heaters could be left on continuously at low power, to prevent ice from forming.
Silica aerogels are typically synthesized by using a sol-gel process. The first step is the creation of a colloidalsuspension of solid particles known as a "sol". The precursors are a liquid alcohol such as ethanol which is mixed with a silicon alkoxide, such as tetramethoxysilane (TMOS), tetraethoxysilane (TEOS), and polyethoxydisiloxane (PEDS) (earlier work used sodium silicates). The solution of silica is mixed with a catalyst and allowed to gel during a hydrolysis reaction which forms particles of silicon dioxide. The oxide suspension begins to undergo condensation reactions which result in the creation of metal oxide bridges (either M–O–M, "oxo" bridges, or M–OH–M, "ol" bridges) linking the dispersed colloidal particles. These reactions generally have moderately slow reaction rates, and as a result either acidic or basic catalysts are used to improve the processing speed. Basic catalysts tend to produce more transparent aerogels and minimize the shrinkage during the drying process and also strengthen it to prevent pore collapse during drying.
Finally, during the drying process of the aerogel, the liquid surrounding the silica network is carefully removed and replaced with air, while keeping the aerogel intact. Gels where the liquid is allowed to evaporate at a natural rate are known as xerogels. As the liquid evaporates, forces caused by surface tensions of the liquid-solid interfaces are enough to destroy the fragile gel network. As a result, xerogels cannot achieve the high porosities and instead peak at lower porosities and exhibit large amounts of shrinkage after drying. To avoid the collapse of fibers during slow solvent evaporation and reduce surface tensions of the liquid-solid interfaces, aerogels can be formed by lyophilization (freeze-drying). Depending on the concentration of the fibers and the temperature to freeze the material, the properties such as porosity of the final aerogel will be affected.
In 1931, to develop the first aerogels, Kistler used a process known as supercritical drying which avoids a direct phase change. By increasing the temperature and pressure he forced the liquid into a supercritical fluid state where by dropping the pressure he could instantly gasify and remove the liquid inside the aerogel, avoiding damage to the delicate three-dimensional network. While this can be done with ethanol, the high temperatures and pressures lead to dangerous processing conditions. A safer, lower temperature and pressure method involves a solvent exchange. This is typically done by exchanging the initial aqueous pore liquid for a CO2-miscible liquid such as ethanol or acetone, then onto liquid carbon dioxide and then bringing the carbon dioxide above its critical point. A variant on this process involves the direct injection of supercritical carbon dioxide into the pressure vessel containing the aerogel. The end result of either process exchanges the initial liquid from the gel with carbon dioxide, without allowing the gel structure to collapse or lose volume.
Resorcinol–formaldehyde aerogel (RF aerogel) is made in a way similar to production of silica aerogel. A carbon aerogel can then be made from this resorcinol–formaldehyde aerogel by pyrolysis in an inert gas atmosphere, leaving a matrix of carbon. The resulting carbon aerogel may be used to produce solid shapes, powders, or composite paper. Additives have been successful in enhancing certain properties of the aerogel for the use of specific applications. Aerogel composites have been made using a variety of continuous and discontinuous reinforcements. The high aspect ratio of fibers such as fiberglass have been used to reinforce aerogel composites with significantly improved mechanical properties.
Silica-based aerogels are not known to be carcinogenic or toxic. However, they are a mechanical irritant to the eyes, skin, respiratory tract, and digestive system. They can also induce dryness of the skin, eyes, and mucous membranes. Therefore, it is recommended that protective gear including respiratory protection, gloves and eye goggles be worn whenever handling or processing bare aerogels, particularly when a dust or fine fragments may occur.
^R. G. Jones; J. Kahovec; R. Stepto; E. S. Wilks; M. Hess; T. Kitayama; W. V. Metanomski (2008). IUPAC. Compendium of Polymer Terminology and Nomenclature, IUPAC Recommendations 2008 (the "Purple Book")(PDF). RSC Publishing, Cambridge, UK.
^Slomkowski, Stanislaw; Alemán, José V.; Gilbert, Robert G.; Hess, Michael; Horie, Kazuyuki; Jones, Richard G.; Kubisa, Przemyslaw; Meisel, Ingrid; Mormann, Werner; Penczek, Stanisław; Stepto, Robert F. T. (2011). "Terminology of polymers and polymerization processes in dispersed systems (IUPAC Recommendations 2011)" (PDF). Pure and Applied Chemistry. 83 (12): 2229–2259. doi:10.1351/PAC-REC-10-06-03. S2CID 96812603.
^A. D. McNaught; A. Wilkinson. (1997). IUPAC. Compendium of Chemical Terminology, 2nd ed. (the "Gold Book") (XML on-line corrected version ed.). Oxford: Blackwell Scientific Publications. doi:10.1351/goldbook. ISBN 978-0-9678550-9-7.
^Definitions of terms relating to the structure and processing of sols, gels, networks, and inorganic-organic hybrid materials (IUPAC Recommendations 2007). Pure and Applied Chemistry. 79. 2007. pp. 1801–1829. doi:10.1351/goldbook.A00173. ISBN 978-0-9678550-9-7. Archived from the original on 30 November 2012.
^"Guinness Records Names JPL's Aerogel World's Lightest Solid". NASA. Jet Propulsion Laboratory. 7 May 2002. Archived from the original on 25 May 2009. Retrieved 25 May 2009.
^Taher, Abul (19 August 2007). "Scientists hail 'frozen smoke' as material that will change world". News Article. London: Times Online. Archived from the original on 12 September 2007. Retrieved 22 August 2007.
^Aegerter, M.A.; Leventis, N.; Koebel, M. M. (2011). Aerogels Handbook. Springer publishing. ISBN 978-1-4419-7477-8.
^ abPajonk, G. M. (16 May 1991). "Aerogel catalysts". Applied Catalysis. 72 (2): 217–266. doi:10.1016/0166-9834(91)85054-Y. ISSN 0166-9834.
^Barron, Randall F.; Nellis, Gregory F. (2016). Cryogenic Heat Transfer (2nd ed.). CRC Press. p. 41. ISBN 9781482227451. Archived from the original on 22 November 2017.
^Kistler, S. S. (1931). "Coherent expanded aerogels and jellies". Nature. 127 (3211): 741. Bibcode:1931Natur.127..741K. doi:10.1038/127741a0. S2CID 4077344.
^Pekala, R. W. (1989). "Organic aerogels from the polycondensation of resorcinol with formaldehyde". Journal of Materials Science. 24 (9): 3221–3227. Bibcode:1989JMatS..24.3221P. doi:10.1007/BF01139044. ISSN 0022-2461. S2CID 91183262.
^"What is Aerogel? Theory, Properties and Applications". azom.com. 12 December 2013. Archived from the original on 9 December 2014. Retrieved 5 December 2014.
^Zhang, Hu; Zhang, Chao; Ji, Wentao; Wang, Xian; Li, Yueming; Tao, Wenquan (30 August 2018). "Experimental Characterization of the Thermal Conductivity and Microstructure of Opacifier-Fiber-Aerogel Composite". Molecules. 23 (9): 2198. doi:10.3390/molecules23092198. ISSN 1420-3049. PMC6225116. PMID30200271.
^Caps, R.; Fricke, J. (2004), Aegerter, Michel A.; Mennig, Martin (eds.), "Aerogels for Thermal Insulation", Sol-Gel Technologies for Glass Producers and Users, Boston, MA: Springer US, pp. 349–353, doi:10.1007/978-0-387-88953-5_46, ISBN 978-0-387-88953-5, retrieved 29 March 2021
^Berge, Axel and Johansson, Pär (2012) Literature Review of High Performance Thermal Insulation Archived 21 November 2014 at the Wayback Machine. Department of Civil and Environmental Engineering, Chalmers University of Technology, Sweden
^Aerogel Structure Archived 25 December 2014 at the Wayback Machine. Str.llnl.gov. Retrieved on 31 July 2016.
^"Silica Aerogel". Aerogel.org. Archived from the original on 4 April 2016.
^The Surface Chemistry of Silica Aerogels Archived 1 December 2014 at the Wayback Machine. Energy.lbl.gov. Retrieved on 31 July 2016.
^Pore Structure of Silica Aerogels Archived 1 December 2014 at the Wayback Machine. Energy.lbl.gov. Retrieved on 31 July 2016.
^ abNguyen, Hong K. D.; Hoang, Phuong T.; Dinh, Ngo T.; Nguyen, Hong K. D.; Hoang, Phuong T.; Dinh, Ngo T. (August 2018). "Synthesis of Modified Silica Aerogel Nanoparticles for Remediation of Vietnamese Crude Oil Spilled on Water". Journal of the Brazilian Chemical Society. 29 (8): 1714–1720. doi:10.21577/0103-5053.20180046. ISSN 0103-5053.
^"Aerogels: Thinner, Lighter, Stronger". NASA. 15 April 2015. Retrieved 29 March 2021.
^Whitwam, Ryan (26 March 2013). Graphene aerogel is world's lightest material Archived 27 March 2013 at the Wayback Machine. gizmag.com
^Quick, Darren (24 March 2013). Graphene aerogel takes world's lightest material crown Archived 25 March 2013 at the Wayback Machine. gizmag.com
^"Metal Oxide Aerogels". Aerogel.org. Archived from the original on 12 August 2013. Retrieved 12 June 2013.
^Kobayashi, Yuri; Saito, Tsuguyuki; Isogai, Akira (2014). "Aerogels with 3D Ordered Nanofiber Skeletons of Liquid-Crystalline Nanocellulose Derivatives as Tough and Transparent Insulators". Angewandte Chemie International Edition. 53 (39): 10394–7. doi:10.1002/anie.201405123. PMID24985785. Lay summary – Royal Society of Chemistry (11 July 2014).
^Passaretti, P., et al. (2019). "Multifunctional graphene oxide-bacteriophage based porous three-dimensional micro-nanocomposites." Nanoscale 11(28): 13318-13329. https://doi.org/10.1039/C9NR03670A
^Biello, David Heavy Metal Filter Made Largely from Air. Archived 26 February 2015 at the Wayback MachineScientific American, 26 July 2007. Retrieved on 2007-08-05.
^ abShi, Mingjia; Tang, Cunguo; Yang, Xudong; Zhou, Junling; Jia, Fei; Han, Yuxiang; Li, Zhenyu (2017). "Superhydrophobic silica aerogels reinforced with polyacrylonitrile fibers for adsorbing oil from water and oil mixtures". RSC Advances. 7 (7): 4039–4045. Bibcode:2017RSCAd...7.4039S. doi:10.1039/C6RA26831E.
^ abcdefgGurav, Jyoti L.; Jung, In-Keun; Park, Hyung-Ho; Kang, Eul Son; Nadargi, Digambar Y. (11 August 2010). "Silica Aerogel: Synthesis and Applications". Journal of Nanomaterials. 2010: 1–11. doi:10.1155/2010/409310.
^Choi, Jinsoon; Suh, Dong Jin (1 September 2007). "Catalytic Applications of Aerogels". Catalysis Surveys from Asia. 11 (3): 123–133. doi:10.1007/s10563-007-9024-2. ISSN 1574-9266. S2CID 97092432.
^Gurav, Jyoti; Jung, In-Keun (30 June 2010). "Silica Aerogel: Synthesis and Applications". Journal of Nanomaterials. 2010: 1–11. doi:10.1155/2010/409310.
^Spoon, Marianne English (25 February 2014). "'Greener' aerogel technology holds potential for oil and chemical clean-up". University of Wisconsin Madison News. Archived from the original on 28 April 2015. Retrieved 29 April 2015.
^"Taking control". Cosmetics Business. 1 April 2006. Retrieved 29 March 2021.
^Chen, Hao; Xu, Yuanming; Tong, Yan; Hu, Junhao (15 March 2019). "The investigation of nanofluidic energy absorption system based on high porosity aerogel nano-materials". Microporous and Mesoporous Materials. 277: 217–228. doi:10.1016/j.micromeso.2018.09.032. ISSN 1387-1811.
^Remington, Bruce A.; Park, Hye-Sook; Casey, Daniel T.; Cavallo, Robert M.; Clark, Daniel S.; Huntington, Channing M.; Kuranz, Carolyn C.; Miles, Aaron R.; Nagel, Sabrina R.; Raman, Kumar S.; Smalyuk, Vladimir A. (10 September 2019). "Rayleigh–Taylor instabilities in high-energy density settings on the National Ignition Facility". Proceedings of the National Academy of Sciences. 116 (37): 18233–18238. doi:10.1073/pnas.1717236115. ISSN 0027-8424. PMC6744876. PMID29946021.
^Hrubesh, Lawrence W. (1 April 1998). "Aerogel applications". Journal of Non-Crystalline Solids. 225 (1): 335–342. Bibcode:1998JNCS..225..335H. doi:10.1016/S0022-3093(98)00135-5.
^Tsou, Peter (2 June 1995). "Silica aerogel captures cosmic dust intact". Journal of Non-Crystalline Solids. Proceedings of the Fourth International Symposium on AEROGELS. 186: 415–427. Bibcode:1995JNCS..186..415T. doi:10.1016/0022-3093(95)00065-8. ISSN 0022-3093.
^"NASA - Catching Comet Dust With Aerogel". NASA. Retrieved 29 March 2021.
^Preventing heat escape through insulation called "aerogel" Archived 13 October 2007 at the Wayback Machine, NASA CPL
^Down-to-Earth Uses for Space Materials Archived 30 September 2007 at the Wayback Machine, The Aerospace Corporation
^Nuckols, M. L.; Chao J. C.; Swiergosz M. J. (2005). "Manned Evaluation of a Prototype Composite Cold Water Diving Garment Using Liquids and Superinsulation Aerogel Materials". United States Navy Experimental Diving Unit Technical Report. NEDU-05-02. Archived from the original on 20 August 2008. Retrieved 21 April 2008.
^Trevino, Luis A.; Orndoff, Evelyne S.; Tang, Henry H.; Gould, George L.; Trifu, Roxana (15 July 2002). "Aerogel-Based Insulation for Advanced Space Suit". SAE Technical Paper Series. 400 Commonwealth Drive, Warrendale, PA, United States: SAE International. 1. doi:10.4271/2002-01-2316.CS1 maint: location (link)
^Iwata, S.; Adachi, I.; Hara, K.; Iijima, T.; Ikeda, H.; Kakuno, H.; Kawai, H.; Kawasaki, T.; Korpar, S.; Križan, P.; Kumita, T. (1 March 2016). "Particle identification performance of the prototype aerogel RICH counter for the Belle II experiment". Progress of Theoretical and Experimental Physics. 2016 (33H01): 033H01. doi:10.1093/ptep/ptw005. ISSN 2050-3911.
^Mulik, Sudhir; Sotiriou-Leventis, Chariklia (2011), Aegerter, Michel A.; Leventis, Nicholas; Koebel, Matthias M. (eds.), "Resorcinol–Formaldehyde Aerogels", Aerogels Handbook, Advances in Sol-Gel Derived Materials and Technologies, New York, NY: Springer, pp. 215–234, doi:10.1007/978-1-4419-7589-8_11, ISBN 978-1-4419-7589-8, retrieved 29 March 2021
^Smirnova I.; Suttiruengwong S.; Arlt W. (2004). "Feasibility study of hydrophilic and hydrophobic silica aerogels as drug delivery systems". Journal of Non-Crystalline Solids. 350: 54–60. Bibcode:2004JNCS..350...54S. doi:10.1016/j.jnoncrysol.2004.06.031.
^Juzkow, Marc (1 February 2002). "Aerogel Capacitors Support Pulse, Hold-Up, and Main Power Applications". Power Electronic Technology. Archived from the original on 15 May 2007.
^"Dunlop Expands Aerogel Line - Tennis Industry". Tennis Industry Magazine. July 2007. Retrieved 29 March 2021.
^Carmichael, Mary. First Prize for Weird: A bizarre substance, like 'frozen smoke,' may clean up rivers, run cell phones and power spaceships. Archived 17 August 2007 at the Wayback Machine Newsweek International, 13 August 2007. Retrieved on 2007-08-05.
^Mazrouei-Sebdani, Z.; Salimian, S.; Khoddami, A.; Shams-Ghahfarokhi, F. (1 August 2019). "Sodium silicate based aerogel for absorbing oil from water: the impact of surface energy on the oil/water separation". Materials Research Express. 6 (8): 085059. Bibcode:2019MRE.....6h5059M. doi:10.1088/2053-1591/ab1eed. ISSN 2053-1591.
^Wang, Fei; Dai, Jianwu; Huang, Liqian; Si, Yang; Yu, Jianyong; Ding, Bin (28 July 2020). "Biomimetic and Superelastic Silica Nanofibrous Aerogels with Rechargeable Bactericidal Function for Antifouling Water Disinfection". ACS Nano. 14 (7): 8975–8984. doi:10.1021/acsnano.0c03793. ISSN 1936-0851. PMID32644778.
^Patel, Prachi (21 August 2020). "Loofah-inspired aerogel efficiently filters microbes from water". Chemical & Engineering News. Retrieved 29 March 2021.
^Halperin, W. P. and Sauls, J. A. Helium-Three in Aerogel. Arxiv.org (26 August 2004). Retrieved on 7 November 2011.
^"De-icing aeroplanes: Sooty skies". The Economist. 26 July 2013. Archived from the original on 30 December 2013. Retrieved 11 December 2013.
^Katakis, Manoli. (11 July 2013) NASA Aerogel Material Present In 2014 Corvette Stingray Archived 22 February 2014 at the Wayback Machine. GM Authority. Retrieved on 2016-07-31.
^Camelbak Podium Ice Insulated Bottle – Review Archived 3 October 2014 at the Wayback Machine. Pinkbike. Retrieved on 31 July 2016.
^Unparalleled Cold Weather Performance Archived 10 January 2016 at the Wayback Machine. 45NRTH. Retrieved on 31 July 2016.
^"Silica Aerogels - an overview". ScienceDirect. Retrieved 29 March 2021.
^Mazrouei-Sebdani, Zahra; Begum, Hasina; Schoenwald, Stefan; Horoshenkov, Kirill V.; Malfait, Wim J. (15 June 2021). "A review on silica aerogel-based materials for acoustic applications". Journal of Non-Crystalline Solids. 562: 120770. Bibcode:2021JNCS..56220770M. doi:10.1016/j.jnoncrysol.2021.120770. ISSN 0022-3093.
^Dorcheh, Soleimani; Abbasi, M. (2008). "Silica Aerogel; Synthesis, Properties, and Characterization". Journal of Materials Processing Technology. 199 (1–3): 10–26. doi:10.1016/j.jmatprotec.2007.10.060.
^ abc"Making silica aerogels". Lawrence Berkeley National Laboratory. Archived from the original on 14 May 2009. Retrieved 28 May 2009.
^Pierre, A. C.; Pajonk, G. M. (2002). "Chemistry of Aerogels and their Applications". Chemical Reviews. 102 (11): 4243–4265. doi:10.1021/cr0101306. PMID12428989.
^Zhang, Xuexia; Yu, Yan; Jiang, Zehui; Wang, Hankun (1 December 2015). "The effect of freezing speed and hydrogel concentration on the microstructure and compressive performance of bamboo-based cellulose aerogel". Journal of Wood Science. 61 (6): 595–601. doi:10.1007/s10086-015-1514-7. ISSN 1611-4663. S2CID 18169604.
^Gan, Yong X.; Gan, Jeremy B. (June 2020). "Advances in Manufacturing Composite Carbon Nanofiber-Based Aerogels". Journal of Composites Science. 4 (2): 73. doi:10.3390/jcs4020073.
^"Carbon Aerogel - an overview | ScienceDirect Topics". ScienceDirect. Retrieved 29 March 2021.
^Thapliyal, Prakash C.; Singh, Kirti (27 April 2014). "Aerogels as Promising Thermal Insulating Materials: An Overview". Journal of Materials. 2014: 1–10. doi:10.1155/2014/127049.
^Cryogel® 5201, 10201 Safety Data Sheet Archived 23 December 2010 at the Wayback Machine. Aspen Aerogels. 13 November 2007
NASA's Stardust comet return mission on AEROGEL.
N. Hüsing; U. Schubert (1998). "Aerogels – Airy Materials: Chemistry, Structure, and Properties". Angewandte Chemie International Edition. 37 (1/2): 22–45. doi:10.1002/(SICI)1521-3773(19980202)37:1/2<22::AID-ANIE22>3.0.CO;2-I.
Pierre A. C.; Pajonk G. M. (2002). "Chemistry of aerogels and their applications". Chemical Reviews. 102 (11): 4243–4266. doi:10.1021/cr0101306. PMID12428989.